The grand prize in the automotive transmission category was won by GKN Sinter Metals, for a carrier and one-way rocker clutch assembly made for Ford Motor Company. Used in the new Ford Super Duty TorqShift six-speed automatic transmission, the hybrid assembly contains five PM steel parts weighing a total of 17 lb. The sinter-brazed subassembly consists of four multi-level PM parts, of which three parts (cage, spider, and carrier plate) are made to a density of 6.8 g/cm3. The rocker plate is sinter-hardened during the sinter-brazing phase and has a density of 7.0 g/cm3. The assembly also has a doubled-pressed and double-sintered cam plate made to 7.3 g/cm3 density with an ultimate tensile strength of 170,000 psi and a mean tempered hardness exceeding 40 HRC. To form the parts and maintain precision tolerances, innovative tooling was developed and used in conjunction with unconventional press motions. Ford subjected the assembly to stringent durability testing-ultimate torsional torque loading at a minimum of 8,000 foot-pounds and fatigue testing at a minimum of 299,000 cycles at 1,730 foot-pounds. The application provided an estimated 20% cost savings over competitive processes, and represents a new era in the scope and size of PM parts.
GKN also won the grand prize in the automotive chassis category for a differential bearing adjuster made for its customer American Axle & Manufacturing and used in the GMT 900 rear differential on GM Tahoe and Yukon models. The diffusion-alloyed PM steel part preloads the bearing and is locked in place through the side holes. Formed to a density of 6.8 g/cm3, it has a 155,000 psi transverse rupture strength, 79,000 psi tensile strength, yield strength of 63,000 psi, and 90 HRB apparent hardness. A special die and dual-upper-punch design form the cross-holes during compaction. Selecting PM saved the customer $320,000 annually by replacing a casting that required extensive machining.
A porous bronze filter made by Capstan California, for Chase Filters and Components received the grand prize in the aerospace/military category. Gravity sintered, the filter is used in an ignition-resistant, fault-tolerant oxygen cryopac filter for medical and emergency breathing systems. The filter's fluted design increases surface area, which in turn increases flow and dirt-holding capacity. The innovative design of the sintering mould allows the retention groove to be formed in the part, eliminating secondary operations. The PM bronze filter replaced a more costly and less reliable stainless steel filter.
Parmatech Corporation, earned the grand prize in the hand tools/recreation category for a large-game 420 stainless steel hunting arrowhead, the 300Xtreem broadhead, made for Optek Precision Tooling Ltd. Fabricated by MIM, the thin blade features a critical straightness necessary for accuracy and the external thread for attachment to the arrow shaft is moulded in the design. The part is formed to a final density of 7.7 g/cm3 and has a 48-52 HRC hardness range. Going the metal injection moulding route saved 50% of the cost of machining the broadhead from stainless steel bar.
A PM copper-steel outer hub exit spindle used in electronic door locks won the grand prize in the hardware/appliances category. Made by ASCO Sintering Company, for Ingersoll Rand Security Technologies (Schlage), the part connects a standard lock and an exit device. When activated through a code or electronic card reader, the spindle rotates to the standard lock assembly.
The PM spindle is made to a 7.7 g/cm3 density and has a 95,000 psi ultimate tensile strength, 8 percent elongation, and 90 HRB hardness. The PM process allowed 95% materials utilization as opposed to machining a wrought blank which yields a materials utilization figure of only 45%. PM also provided a 90% energy savings.
FloMet LLC earned the grand prize in the medical/dental category for a housing cup and lid used in an audio device with magnetic shielding capabilities. This application is the first of its kind in the high-power audio device sector. The anti-magnetic MIM material with high nickel content provides electromagnetic interference, or EMI shielding, preventing interference from other electronic signal sources. While the cup has four thin walls for proper assembly, the new lid design must fit securely into the cup opening; this prevents moisture and/or foreign matter from entering the housing, as well as maintaining the EMI shielding capability. Manufactured to 8.30 g/cm3 density, the parts have an ultimate tensile strength of 84,000 psi, yield strength of 32,000 psi, and a 40% elongation.
Awards of distinction
Cloyes Gear & Products, Inc. won the award of distinction in the automotive engine market category for an intake sprocket gear and an exhaust gear used in a coupling assembly operating in 2.0 and 2.2 litre diesel engines made by General Motors Korea. The gears receive torque from the timing chain, which drives the intake camshaft and transmits torque to the exhaust camshaft. The exhaust gear, also called a "scissor gear," is an anti-backlash gear, which reduces backlash and mediates engine noise, vibration, and harshness. Warm compacted to a 7.2 g/cm3 minimum density on the teeth, the PM steel gears have an ultimate tensile strength of 196,000 psi, typical yield strength of 161,000 psi, a fatigue limit of 55,000 psi, and 74 HRA hardness after carburizing.
A rear sight used on sporting and military rifles such as the AR-15, M4, and M16 models, received the award of distinction in the aerospace/military market category. Made by Megamet Solid Metals, Inc. for its customer, Yankee Hill Machine Co Inc, the nickel steel MIM part features very close tolerances and a complex geometry requiring an elaborate tool design. The part is made to a density of 7.5 g/cm3 and has an as-sintered ultimate tensile strength of 55,000 psi. Choosing the MIM process over investment casting provides a 40% cost savings.
Bangalore, India-based Indo-US MIM Tec (P) Ltd won an award of distinction in the hand tools/recreation market category for a 17-4PH stainless steel hammer used in a Leatherman Tool Group multi-purpose military utility tool (MUT) designed for military and law enforcement personnel, and civilians. Made by the MIM process, the intricate complex part is formed to a density of 7.5 g/cm3 and has an ultimate tensile strength of 175,000 psi, yield strength of 158,000 psi, heat-treated 35-40 HRC hardness, and a minimum six percent elongation.
Webster-Hoff Corporation, and customer ACCO Brand Inc. received the second award of distinction in the hand tools/recreation market category for a PM sinter-hardened steel cam and bushing used in a manual paper hole punching machine. The cam transfers power to the cutters and the bushing supports the shaft. Both parts are formed to a density of 6.7 g/cm3 and have an ultimate tensile strength of 120,000 psi and 27 HRC apparent hardness. Formed to a net shape, the parts are sinter-hardened and tempered. The cam receives a vibro finishing operation and vacuum oil treatment.
Burgess-Norton Mfg Co earned the award of distinction in the hardware/appliances category for a PM steel crimp retainer operating in a valve assembly that regulates gas flow in a high-performance compressor for commercial refrigerators. Formed to a minimum density of 7.1 g/cm3, the part has a minimum ultimate tensile strength of 160,000 psi, yield strength of 150,000 psi, and 74 HRA hardness. The part's outside diameter is designed with a smooth flowing radius to permit gas flow around it with minimal turbulence. Picking PM offered a 30 to 50% cost savings over competing fabricating processes such as casting or stamping.
A 17-PH stainless steel distal channel retainer formed via the MIM process by Kinetics Climax, Inc. received the award of distinction in the medical/dental market category. The complex, multi-level part is the main distal-side component of an articulation joint in an articulating mechanical stapler/cutter used in endoscopic surgery.
Formed to a typical density of 7.7 g/cm3, the part has a typical tensile strength of 175,000 psi, yield strength of 158,000 psi, and a six percent elongation. The MIM process provided a cost savings in the range of 25 to 30% versus other design options.
A bronze filter plate made by Capstan California, Carson, Calif., for Knorr-Bremse GmbH in Austria won an award of distinction in the off-highway category. Made via the gravity sintering process, the net-shape part is used in the braking system of European commuter trains. A graphite mould design incorporates the 8.2 mm cross-hole, which eliminates a machining operation for drilling the hole. The burr-free design required 8.8% less material than the competitive process and reduced the cost of the part by 27%.